Fabrication of Semiconductor Device Using Alternating High and Low Temperature Layers

ABSTRACT

A method for fabricating a III-nitride semiconductor body that includes high temperature and low temperature growth steps.

RELATED APPLICATION

This application is based on and claims benefit of U.S. Provisional Application Ser. No. 60/717,102, filed on Sep. 14, 2005, entitled Process For Manufacture of Super Lattice Using Alternating High and Low Temperature Layers to Block Parasitic Current Path, to which a claim of priority is hereby made and the disclosure of which is incorporated by reference.

DEFINITION

III-nitride as used herein refers to a semiconductor alloy from the InAlGaN system that includes at least Nitrogen and another alloying element from group Examples of a III-nitride alloy are MN, GaN, AlGaN, InGaN, InAlGaN, or any combination that includes nitrogen or at least one element from group III.

BACKGROUND OF THE INVENTION

The present invention relates to a process for fabricating a power semiconductor device and more particularly a III-nitride power semiconductor device.

A well known III-nitride power semiconductor device includes a substrate, a III-nitride transition layer, and a heterojunction III-nitride device over the transition layer. Such devices have been known to include a parasitic conduction path from Ser. No. 00/784,146.1 the heterojunction device to the substrate. The parasitic conduction path is undesirable in that it undermine the ability of the device to switch current effectively.

It is desirable to minimize the effect of or to eliminate the parasitic conduction path in III-nitride heterojunction devices.

SUMMARY OF THE INVENTION

It is an object of the present invention to provide a process for fabrication of a III-nitride power semiconductor device which does not include a parasitic conduction path.

It is believed that the parasitic conduction as explained above is defect assisted. Therefore, a process according to the present invention involves a method that minimize the defects which assist in the promotion of parasitic conduction paths.

Specifically, a method according to the present invention includes providing a substrate, and growing a III-nitride body over a major surface of the substrate to a final thickness over a growth period of time, wherein the growth temperature is varied over the growth period of time.

In one variation of the present invention, the growth temperature is varied in cycles, each cycle including a period of high temperature growth at a high temperature and a period of low temperature growth at a low temperature.

In one embodiment of the present invention, the high temperature and the low temperature in all cycle are the same.

In another embodiment of the present invention, the low temperature in each cycle is varied, while the high temperature remains the same from cycle to cycle.

In yet another embodiment of the present invention, the low temperature and the high temperature are varied in each cycle until the two temperatures converge.

In all of the embodiments, the period of time for the low temperature or the high temperature in each cycle can be varied as desired.

In another variation of the present invention, the growth temperature is continuously varied either in an ascending direction or in a descending direction.

Other features and advantages of the present invention will become apparent from the following description of the invention which refers to the accompanying drawings.

BRIEF DESCRIPTION OF THE DRAWING(S)

FIGS. 1A and 1B illustrate a method according to the first embodiment of the present invention.

FIGS. 2A and 2B illustrate a method according to the second embodiment of the present invention.

FIGS. 3A and 3B illustrate a method according to the third embodiment of the present invention.

FIGS. 4A and 4B illustrate a method according to the fourth embodiment of the present invention.

FIG. 5 schematically illustrates an example of a III-nitride device fabricated according to the present invention.

DETAILED DESCRIPTION OF THE FIGURES

Referring to FIGS. 1A-1B, in a process according to the first embodiment of the present invention a III-nitride super lattice body 10 (e.g. AlN body) is grown on a substrate 12 by varying the growth temperature over a growth period of time. Specifically, the growth temperature is varied in cycles, each cycle 14 including a period of high temperature growth followed by a period of low temperature growth. Thus, as illustrated in FIG. 1A graphically a III-nitride semiconductor body is grown for a first period of time 16 at a high temperature T₁ (e.g. 1000° C.), and then another III-nitride body is grown for a second period of time 18 at a lower temperature T₂ (e.g. 800° C.). Growth cycle 14 is then repeated until a III-nitride super lattice body of a desired thickness is obtained.

It should be noted that it has been observed that the best results can be achieved if a process according to the present invention starts with a low temperature growth step first. Thus, it is preferred that a process according to the present invention starts with a low temperature growth step and then followed with other steps as explained in relation to the embodiments described below.

In a method according to the first embodiment, high growth temperature T₁ in all cycles are equal to one another, and low growth temperature T₂ in all cycles are equal to one another. Note that first period of time 16 in all cycles may be equal to one another and even equal to second period of time 18 in all cycles. Similarly, second period of time in all cycles 14 may be equal to one another. First and second periods of time 16, 18 may also be varied as desired.

Referring to FIGS. 2A and 2B, in a method according to the second embodiment of the present invention, high growth temperature T₁ in all cycles 14 are equal, while low growth temperatures T₂, T₃, T₄, . . . T_(N) (N=an integer representing the last III-nitride body formed during a low temperature growth step) are different from one another. Preferably, low growth temperatures start from a low value (T₁) and are increased in each step to a higher temperature.

Referring now to FIGS. 3A and 3B, in a method according to the third embodiment of the present invention, high growth temperature and low growth temperature in each cycle is varied, whereby preferably the two growth temperatures converge with every cycle. Thus, in the first cycle T₁ is the high growth temperature while T₂ is the low growth temperature. In the next cycle T₃ is the high growth temperature and T₄ is the low growth temperature. The cycles are repeated until T_(X) (last high growth temperature) and T_(Y) (last low growth temperature are reached). To converge the two growth temperatures the high growth temperature is lowered while the low growth temperature is increased in each cycle. Thus, T₁>T₃ while T₂<T₄ until preferably a final growth temperature T_(f) is reached after reaching T_(X) and T_(Y).

Referring now to FIGS. 4A and 4B, in a method according to the fourth embodiment of the present invention, the growth temperature is varied continuously until a desired thickness is obtained. For example, the growth temperature can start from a high value and descend continuously to a low value (curve 20) or start from a low growth temperature and ascend to a high value (curve 22).

Referring to FIG. 5, a III-nitride device can be formed over a III-nitride super lattice that is formed according to the present invention. For example, a device can be formed over a III-nitride super lattice 10 that is formed according to the third embodiment of the present invention (or other embodiments) as illustrated in FIG. 5. Such a III-nitride device may include a III-nitride transition layer (or layers) 24, a III-nitride buffer layer 26, and a III-nitride active layer 28 which may constitute the active region for a high electron mobility transistor (HEMT). It should be noted that a device according to the present invention is not limited to a HEMT. Other devices such as III-nitride MISFETs, MISHFETs, HEMFETs, HJFET or the like may also be formed on a III-nitride super lattice 10 formed according to the present invention.

Furthermore, it should be noted that in a process according to the present invention the alloy composition can be changed as the temperature is varied. Thus, for example, the alloy composition of one III-nitride semiconductor body grown at a high temperature can be different from the alloy composition of another III-nitride body grown at a low temperature. In another variation, the alloy composition in the body of a III-nitride body grown at high temperature or low temperature can be varied as well; i.e. a III-nitride body can have a varying alloy composition.

In a method according to the present invention substrate 12 may be composed of silicon, sapphire, a III-nitride substrate such as a GaN substrate, silicon carbide or the like. Silicon, however, is a preferred substrate for economic reasons.

Although the present invention has been described in relation to particular embodiments thereof, many other variations and modifications and other uses will become apparent to those skilled in the art. It is preferred, therefore, that the present invention be limited not by the specific disclosure herein, but only by the appended claims. 

1-21. (canceled)
 22. A method of fabricating a semiconductor device, said method comprising: providing a substrate; growing a III-nitride body over a major surface of said substrate to a final thickness over a growth period of time, wherein a growth temperature is varied over said growth period of time; said III-nitride body comprising at least two AlN layers grown at different temperatures.
 23. The method of claim 22, wherein said III-nitride body further comprises a superlattice.
 24. The method of claim 22, wherein said III-nitride body further comprises a superlattice, and wherein a number of layers grown at a high temperature is equal to a number of layers grown at a low temperature.
 25. The method of claim 22, wherein said growth temperature is varied in cycles over said growth period of time, each cycle including a period of a high temperature and a period of a low temperature.
 26. The method of claim 22, further comprising forming a buffer layer over said III-nitride body.
 27. The method of claim 26, further comprising forming an active layer over said buffer layer, said active layer providing an active region for fabricating a power FET.
 28. The method of claim 25, wherein said low temperature in each cycle is varied.
 29. The method of claim 25, wherein said high temperature in each cycle is varied.
 30. The method of claim 25, wherein said low temperature and said high temperature in each cycle are varied.
 31. The method of claim 25, wherein said high temperature in each cycle is the same.
 32. The method of claim 25, wherein said low temperature in each cycle is the same.
 33. The method of claim 22, wherein a period of high temperature growth is varied.
 34. The method of claim 22, wherein a period of low temperature growth is varied.
 35. The method of claim 22, wherein a period of high temperature growth and a period of low temperature growth are varied.
 36. The method of claim 22, wherein a period of high temperature growth is equal to a period of low temperature growth.
 37. The method of claim 22, wherein a period of high temperature growth is different than a period of low temperature growth.
 38. The method of claim 22, wherein said growth temperature is varied continuously.
 39. The method of claim 22, wherein said growth temperature is varied in discrete steps.
 40. The method of claim 24, wherein said low temperature in each cycle is varied.
 41. The method of claim 24, wherein said high temperature in each cycle is varied. 